1.4542 Uns S17400 630 17-4pH Precipitation Martensitic Brushed Stainless Steel Rod Bar
Product Details:
| Place of Origin: | CHINA |
| Brand Name: | ZHEMU |
| Certification: | ISO |
| Model Number: | Standard and Customization |
Payment & Shipping Terms:
| Minimum Order Quantity: | Not limited |
|---|---|
| Price: | As Per Quotation |
| Packaging Details: | Plywood Box |
| Delivery Time: | 25-35 days |
| Payment Terms: | T/T |
| Supply Ability: | 5000kg per Week |
|
Detail Information |
|||
| Name: | 1.4542 Uns S17400 630 17-4pH Precipitation Hardening Martensitic Stainless Steel | Grade: | Stainless Steel |
|---|---|---|---|
| Shape: | ±1% | Model NO.: | 1.4542 UNS S17400 630 17-4PH |
| Type: | Round/Square/Hexagon/Flat Bar | Processing: | Hot/Cold Rolling |
| Surface: | Black Or Bright Or Pickling White | Size Range: | Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm |
| Similar Grade: | 1.4542 Uns S17400 630 17-4pH | ||
| High Light: | 1.4542 Uns S17400,brushed stainless steel rod,brushed steel bar |
||
Product Description
Mill′s test certificate:
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Quality Standard:
ASTM A564 2004 Standard Specification for Hot Rolled and Cold Finished Age Hardening Stainless Steel Bars and Shapes
ASTM A705 Standard Specification for Age Hardening Stainless Steel Forgings
Introduction:
15-5PH is a martensitic precipitation-hardening stainless steel that provides high strength, good
corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C) and good toughness in both the longitudinal and transverse directions in both base metal and welds. Short-time, low-temperature heat treatments minimize distortion and scaling.
15-5PH is the ferrite-free version of 17-4PH Stainless Steel. Both alloys are widely used in the
aerospace, chemical, petrochemical, food processing, paper and general metalworking industries.
Applications:
Aircraft components
High pressure corrosive fabricated parts such as valves
Shafts
Fasteners
Fittings and gears
Similar Grade:
DIN |
ASTM | UNS | CNU |
| 1.4545 | XM-12 | S15500 | 15-5PH |
Chemical Composition(%)
C |
Si | Mn | P | S | Cr | Ni | Cu | Nb+Ta |
| 0.07 max | 1.0 max | 1.0 max | 0.030 max | 0.035 max | 14.0-15.0 | 3.5-5.5 | 2.5-4.5 | 0.15-0.45 |
Mechanical Properties
Delivery Condition |
Modulus of Elasticity (GPa) |
Modulus of Rigidity (GPa) |
Tensile Strength Rm (Mpa) | Yield Strength Rp0.2(Mpa) | Elongation % in 2″ (50.8 mm) | Reduction Of Area (%) |
Hardness (HRC) |
| A(annealed) | / | / | / | / | / | / | 35 max |
| H 900 | 197.6 | 77.3 | 1378 min | 1276 min | 14 min | 50 min | 44 min |
| H925 | / | / | 1309 min | 1207 min | 14 min | 54 min | 42 min |
| H1025 | / | 75.9 | 1173 min | 1138 min | 15 min | 56 min | 38 min |
| H1075 | / | 69 | 1138 min | 1035 min | 16 min | 58 min | 36 min |
| H1100 | / | / | 1035 min | 931 min | 17 min | 58 min | 34 min |
| H1150 | / | 69 | 1000 min | 862 min | 19 min | 60 min | 33 min |